Soldering to Magnet Wires with 50In50Pb Alloy


Reading time ( words)

Posted by Derrick Herron on Monday, October 20, 2014



The Indium Corporation recently had a customer contact us looking for 50In50Pb solder wire.  We manufacture large amounts of this indium-lead material as it is used in numerous applications.  In this case, it was the application that was quite interesting.  I won’t give any customer information, but will say that a report by Hughes Aircraft was brought to our attention.  It can be found online here. The report deals with the bonding of extremely thin copper wire (down to 0.0004” in diameter!) to thicker, more resilient wire.spool_indium.jpg

Through the work done in the above-mentioned paper, it was found that the 50In50Pb formed the strongest bond of the alloys tested and was very limited in its consumption of the copper wire when manufacturing times and temperatures were carefully observed. I was sure to caution our customer that indium and copper will form a brittle intermetallic layer, as my colleague Eric Bastow explains here. However, Eric also points out that this type of solder joint is created every day in applications where it does not cause a problem to the end product. In any application, reliability testing should be done to ensure that the final product exceeds the needs of the environment in which it will be used.  We were curious if more people out there are using indium-lead solder alloys in this type of application.The thicker wire is able to withstand the stresses placed on it in a subsequent encapsulation step, whereas the thin copper wire would break during this step, therefore making the thicker material necessary.  One problem that quickly arose was that if traditional tin-based solders were used to bond these two wires together, they would very rapidly consume the thin copper wire, resulting in an extremely weak interface - if an interface survived at all.  An alternate solder was needed and 50In50Pb was my recommendation.

Please send me a message if you’re doing this type of work or if you’re interested in using our indium-lead alloys for this or any other application. -Derrick

derrick_herron.jpg 

Derrick Herron

Contact Derrick

315-853-4900 x7599

Capture-derrickbuttons.JPG

Share

Print


Suggested Items

Just Ask Joe: The Occam Process

08/25/2020 | I-Connect007 Editorial Team
First, we asked you to send in your questions for Happy Holden. Now, it’s Joe Fjelstad’s turn! Inventor, columnist, instructor, and founder of Verdant Electronics, Joe has been involved with rigid PCBs and flexible circuits for decades, and he’s ready to share some of his knowledge with our readers. We hope you enjoy “Just Ask Joe.”

The iNEMI 2019 Board Assembly Roadmap

06/01/2020 | Pete Starkey, I-Connect007
iNEMI continues to publish chapters of its 2019 Roadmap and recently presented an overview of its Board Assembly Roadmap Chapter in a webinar prefaced by Grace O’Malley, vice president of global operations. The new chapter is just the latest addition to this global effort from 23 working groups contributing expert input from all aspects of the electronics industry.

Joe Fjelstad Breaks Down His Occam Process

03/04/2020 | I-Connect007 Editorial Team
Joe Fjelstad recently met with the I-Connect007 Editorial Team to discuss the potential benefits of his Occam process for solderless assembly. This technique allows assembly of the PCB without the risks associated with traditional surface-mount processes, such as solder joint failure. Has the time come for the industry to embrace Occam?



Copyright © 2020 I-Connect007. All rights reserved.